Nom du produit: Tuyau d'acier inoxydable d'alliage de nickel et de cuivre-nickel, tuyau d'alliage de Nickel-cuivre, tubes de cuivre sans couture
DIAMÈTRE EXTÉRIEUR: 8-2500MM, (3/8 "-100")
ÉPAISSEUR DE PAROI: 0.3-150MM,(SCH10-XXS)
LONGUEUR: 2000MM, 2438MM, 3000MM, 5800MM, 6000MM,12000MM, ETC
NORME: ASTM B68/B88/B75/B111,JIS H3300, BS2871, EN1057, EN12449, ETC
Surface: Ba,2b,No.1,No.4,4k,Hl,8k
Certification: ISO, SGS,BV
Technique: Laminé à chaud laminé à froid
Grade(Astm Uns):N04400 、 N05500 、 N4 、 N6 、 254smo 、 17-4ph 、 2507 、 904l 、 304 、 304l 、 303 、 316l 、 317l 、 S60 、 347h 、 309s 、 316s 、 904l 、 S32205 、 2507 、 254smos s31635 、 S31254 、 N08926 、 2205 、 S32205 、 S31008 、 S30908 、 S32750 、 S32760 、 630 Etc
Catégorie (En): 1,4301, 1,4307, 1,4541, 1,4401, 1,4404, 1,4571, 1,4438, 1,4539, 1,4547, 1,4529, 1,4410, 1,4501, 1,4462, 1,4845, 1,4542,, etc
Nom du produit: Tuyau d'acier inoxydable d'alliage de nickel et de cuivre-nickel
Diamètre extérieur: 8-2500mm, (3/8 "-100")
Épaisseur: 0.3-150mm,(Sch10-Xxs)
Longueur: 2000mm, 2438mm, 3000mm, 5800mm, 6000mm,12000mm, etc
Norme: Astm,Aisi,Jis,Gb, Din,En
Surface: Ba,2b,No.1,No.4,4k,Hl,8k
Certification: Iso, Sgs,Bv
Technique: Laminé à chaud laminé à froid
Grade(Astm Uns):N04400 、 N05500 、 N4 、 N6 、 254smo 、 17-4ph 、 2507 、 904l 、 304 、 304l 、 303 、 316l 、 317l 、 S60 、 347h 、 309s 、 316s 、 904l 、 S32205 、 2507 、 254smos s31635 、 S31254 、 N08926 、 2205 、 S32205 、 S31008 、 S30908 、 S32750 、 S32760 、 630 Etc
Catégorie (En): 1,4301, 1,4307, 1,4541, 1,4401, 1,4404, 1,4571, 1,4438, 1,4539, 1,4547, 1,4529, 1,4410, 1,4501, 1,4462, 1,4845, 1,4542,, etc
Alliages de cuivre-nickel
Tuyaux sans soudure en cuivre-nickel 70/30
Tuyaux sans soudure Cupro Nickel 70/30, Uns C71500 Tuyaux sans soudure, Din 2.0882 Tuyaux sans soudure
Tubes sans soudure cuivre-nickel 70/30
Tube sans couture Cu-Ni 70/30, Tubes sans soudure Cuni Uns C71500, Tubes sans soudure Din 2.0882
Tuyaux soudés cuivre-nickel 70/30
Fournisseur de tuyaux soudés Cupro Nickel 70/30, Tuyaux soudés Uns C71500, Tuyau soudé Cu-Ni Din 2.0882
Tubes soudés en cuivre-nickel 70/30
Tubes soudés Cuni 70/30, Tube soudé Uns C71500, Asme Sb111 Cuivre Nickel 70/30 Tubes soudés
Tuyaux Erw 70/30 Cuivre Nickel
Cupro Nickel 70/30 Erw Pipe Fournisseur, Cuni Alloy Uns C71500 Erw Pipes, Cu-Ni Din 2.0882 Erw Pipe
Tubes Erw Cuivre Nickel 70/30
Tube Erw d'Uns C71500, tuyauterie d'Erw du Din 2.0882, tubes d'Erw du nickel 70/30 d'Astm B111 Cupro, tubes de Cu-Ni 70/30 Erw
Tubes 90/10 de nickel de Cupro pour des échangeurs de chaleur et des condenseurs
Tubes 90/10 de nickel de Cupro pour le nickel 90/10 de Industriescopper d'automobile tuyaux sans couture
Tuyaux sans soudure Cupro Nickel 90/10, Uns C70600 Tuyaux sans soudure, Din 2.0872 Tuyaux sans soudure
Tubes sans soudure cuivre nickel 90/10
Tube sans couture Cu-Ni 90/10, Tubes sans soudure Cuni Uns C70600, Tubes sans soudure Din 2.0872
Tuyaux soudés cuivre-nickel 90/10
Fournisseur de tuyaux soudés Cupro Nickel 90/10, Tuyaux soudés Uns C70600, Tuyau soudé Cu-Ni Din 2.0872
Tubes soudés en cuivre-nickel 90/10
Tubes soudés 90/10 Cuni, Tube soudé Uns C70600, Asme Sb111 Cuivre Nickel 90/10 Tubes soudés
Tuyaux Erw 90/10 Cuivre-Nickel
Cupro Nickel 90/10 Erw Pipe Fournisseur, Cuni Alloy Uns C70600 Erw Pipes, Cu-Ni Din 2.0872 Erw Pipe
Cuivre Nickel 90/10 Erw Tubes
Tube d'Uns C70600 Erw, tuyauterie de Din 2.0872 Erw, tubes du nickel 90/10 Erw d'Astm B111 Cupro, tubes de Cu-Ni 90/10 Erw
Le passage aux tubes en cuivre-nickel
Cuivre avait été prouvé depuis les premiers jours pour avoir beaucoup de bons attributs. Il était facile de se plier et avait
Résistance à la corrosion très élevée, mais il y avait des inquiétudes au sujet de sa faible résistance à la corrosion-fatigue. Quand le cupro
Le nickel a été présenté, il a montré la résistance à la corrosion semblable au cuivre, résistance générale plus élevée et mieux
Force de fatigue.
Propriétés de la tuyauterie de frein de cuivre-nickel
L'alliage cuivre-nickel utilisé pour les tubes de frein contient généralement 10% de nickel, avec du fer et du manganèse
De 1,4% et 0,8% respectivement. Le produit est conforme à astm b466 (société américaine pour les tests
Et matériaux), qui spécifie les dimensions, la résistance à la traction et la limite d'élasticité. Formabilité et interne
Propreté conforme aux spécifications sae j527, astm a254 et smt c5b (société de moteur
Fabricants et commerçants). Également, l'alliage répond aux exigences de confinement de pression, de fabrication
Et résistance à la corrosion pour iso 4038 (organisation internationale de normalisation) et sae j1047.
Cupronickel ou cuivre-nickel ou "cupernickel" est un alliage de cuivre qui contient du nickel et le renforcement
Éléments, tels que le fer et le manganèse. Cupronickel est très résistant à la corrosion dans l'eau de mer, parce que son
Potentiel d'électrode est ajusté pour être neutre par rapport à l'eau de mer. Pour cette raison, il est utilisé pour la tuyauterie, la chaleur
Échangeurs et condenseurs dans les systèmes d'eau de mer, ainsi que le matériel marin, et parfois pour les hélices,
Vilebrequins et coques de remorqueurs premium, bateaux de pêche et autres bateaux de travail.
Cupronickel autres noms commerciaux enregistrés sont alpaka ou alpacca' (marque déposée), argentan minargent, et
Le nom français cuivre blanc. De temps en temps, le cupronickel est également appelé "hotel silver", plata alemana
(Espagnol pour "argent allemand"), "argent allemand" et "argent chinois".
Parfois appelé cupro-nickels, il existe une gamme de différents alliages cuivre-nickel qui possèdent différents
Propriétés et par conséquent sont adaptés à une gamme de différentes applications. Certains des alliages de cuivre-nickel les plus connus
Comprennent:
Cuivre avec 10% de nickel
Cuivre avec 30% nickel
Cuivre avec 25% de nickel avec 0, 05-0, 4% de manganèse
Cuivre avec 45% de nickel (également connu sous le nom de constantan)
Chemical Composition of Copper Nickel 70/30 Pipes & Tubes
Grade |
Cu |
Mn |
Pb |
Ni |
Fe |
Zn |
Cu-Ni 70-30 |
65.0 min |
1 max |
.05 max |
29-33 |
0.4-1.0 |
1 max |
Mechanical Properties of Cu-Ni 70/30 Pipes and Tubing
Properties |
Metric |
Imperial |
Tensile strength, ultimate |
372-517 MPa |
54000-75000 psi |
Tensile strength, yield (depending on temper) |
88.0-483 MPa |
12800-70100 psi |
Elongation at break (in 381 mm) |
45.0% |
45.0% |
Charpy impact |
107 J |
78.9 ft-lb |
Machinability (UNS C36000 (free-cutting brass) = 100%) |
20% |
20% |
Shear modulus |
57.0 GPa |
8270 ksi |
Poisson's ratio |
0.34 |
0.34 |
Elastic modulus |
150 GPa |
21800 ksi |
Physical Properties of Cupro Nickel 70/30 Pipes & Tubes
Properties |
Metric |
Imperial |
Density |
8.94 g/cm3 |
0.323 lb/in3 |
Melting point |
2140°F |
1171°C |
Chemical Composition of Copper Nickel 90/10 Pipes & Tubes
Grade |
Cu |
Mn |
Pb |
Ni |
Fe |
Zn |
Cu-Ni 90-10 |
88.6 min |
1.0 max |
.05 max |
9-11 max |
1.8 max |
1 max |
Mechanical Properties of Cu-Ni 90/10 Pipes and Tubing
Properties |
Metric |
Imperial |
Tensile strength, ultimate |
303-414 MPa |
43900-60000 psi |
Tensile strength, yield (depending on temper) |
110-393 MPa |
16000-57000 psi |
Elongation at break (in 254 mm) |
42.00% |
42.00% |
Machinability (UNS C36000 (free-cutting brass) = 100%) |
20% |
20% |
Shear modulus |
52.0 GPa |
7540 ksi |
Poisson's ratio |
0.34 |
0.34 |
Elastic modulus |
140 GPa |
20300 ksi |
Physical Properties of Cupro Nickel 90/10 Pipes & Tubes
Properties |
Metric |
Imperial |
Density |
8.94 g/cm3 |
0.323 lb/in3 |
All copper nickel alloys consist of only one phase as the copper nickel binary system exhibits complete solid solubility
Applications of Copper Nickel alloys:
Sea Water Condensor Systems And Desalination Plants
Due to the good resistance to sea water corrosion, the copper nickel alloy Copper 90/10 and copper nickel alloy Copper 70/30 are employed for sea water condenser systems and in desalination plants, as well as pipe work in chemical plants.
Automotive Applications
Due to the fact that the copper nickel alloy Copper 90/10 requires no surface protection and hence gives extra safety, this copper nickel alloy is being increasingly employed for brake and hydraulic suspension systems and cooling systems in cars and commercial vehicles.
Marine Applications
The good resistance to biofouling and sea water corrosion resistance of the copper nickel alloys, Copper 90/10 and Copper 70/30 alloys have lead to its use in applications such as cladding for ships' hulls, legs of oil rig platforms and sea water intake screens.
Coins
The copper nickel alloys composed of copper with 25% nickel with 0.05-0.4% manganese is commonly used for the manufacture of coins, medals and other semi valuable applications.
Resistance Wire
Due to the very low temperature co-efficient of electrical resistivity, the copper nickel alloys composed of copper with 45% nickel alloy is used for resistance wire in high precision resistors. This property of copper nickel alloys allows the resistor to operate at almost exactly the same resistance regardless of temperature.
Thermocouples
The copper nickel alloys composed of copper-45% nickel alloy is also used for thermocouples as it develops a high and uniform EMF when coupled with other metals such as copper and iron.
Other
Copper nickel alloys are also used in cooling circuits, ammunition, sea water corrosion-resistant assemblies, condenser tubes. Other Applications"
Desalination units
Property Table of Copper Nickel Alloys
lammability |
5 |
Fresh Water |
5 |
Organic Solvents |
5 |
Oxidation at 500C |
3 |
Sea Water |
5 |
Strong Acid |
2 |
Strong Alkalis |
5 |
UV |
5 |
Wear |
5 |
Weak Acid |
4 |
Weak Alkalis |
5 |
Le passage aux tubes en cuivre-nickel
Cuivre avait été prouvé depuis les premiers jours pour avoir beaucoup de bons attributs. Il était facile de se plier et avait
Résistance à la corrosion très élevée, mais il y avait des inquiétudes au sujet de sa faible résistance à la corrosion-fatigue. Quand le cupro
Le nickel a été présenté, il a montré la résistance à la corrosion semblable au cuivre, résistance générale plus élevée et mieux
Force de fatigue.
Propriétés de la tuyauterie de frein de cuivre-nickel
L'alliage cuivre-nickel utilisé pour les tubes de frein contient généralement 10% de nickel, avec du fer et du manganèse
De 1,4% et 0,8% respectivement. Le produit est conforme à astm b466 (société américaine pour les tests
Et matériaux), qui spécifie les dimensions, la résistance à la traction et la limite d'élasticité. Formabilité et interne
Propreté conforme aux spécifications sae j527, astm a254 et smt c5b (société de moteur
Fabricants et commerçants). Également, l'alliage répond aux exigences de confinement de pression, de fabrication
Et résistance à la corrosion pour iso 4038 (organisation internationale de normalisation) et sae j1047.
Cupronickel ou cuivre-nickel ou "cupernickel" est un alliage de cuivre qui contient du nickel et le renforcement
Éléments, tels que le fer et le manganèse. Cupronickel est très résistant à la corrosion dans l'eau de mer, parce que son
Potentiel d'électrode est ajusté pour être neutre par rapport à l'eau de mer. Pour cette raison, il est utilisé pour la tuyauterie, la chaleur
Échangeurs et condenseurs dans les systèmes d'eau de mer, ainsi que le matériel marin, et parfois pour les hélices,
Vilebrequins et coques de remorqueurs premium, bateaux de pêche et autres bateaux de travail.
Cupronickel autres noms commerciaux enregistrés sont alpaka ou alpacca' (marque déposée), argentan minargent, et
Le nom français cuivre blanc. De temps en temps, le cupronickel est également appelé "hotel silver", plata alemana
(Espagnol pour "argent allemand"), "argent allemand" et "argent chinois".
Parfois appelé cupro-nickels, il existe une gamme de différents alliages cuivre-nickel qui possèdent différents
Propriétés et par conséquent sont adaptés à une gamme de différentes applications. Certains des alliages de cuivre-nickel les plus connus
Comprennent:
Cuivre avec 10% de nickel
Cuivre avec 30% nickel
Cuivre avec 25% de nickel avec 0, 05-0, 4% de manganèse
Cuivre avec 45% de nickel (également connu sous le nom de constantan)
Chemical Composition of Copper Nickel 70/30 Pipes & Tubes
Grade |
Cu |
Mn |
Pb |
Ni |
Fe |
Zn |
Cu-Ni 70-30 |
65.0 min |
1 max |
.05 max |
29-33 |
0.4-1.0 |
1 max |
Mechanical Properties of Cu-Ni 70/30 Pipes and Tubing
Properties |
Metric |
Imperial |
Tensile strength, ultimate |
372-517 MPa |
54000-75000 psi |
Tensile strength, yield (depending on temper) |
88.0-483 MPa |
12800-70100 psi |
Elongation at break (in 381 mm) |
45.0% |
45.0% |
Charpy impact |
107 J |
78.9 ft-lb |
Machinability (UNS C36000 (free-cutting brass) = 100%) |
20% |
20% |
Shear modulus |
57.0 GPa |
8270 ksi |
Poisson's ratio |
0.34 |
0.34 |
Elastic modulus |
150 GPa |
21800 ksi |
Physical Properties of Cupro Nickel 70/30 Pipes & Tubes
Properties |
Metric |
Imperial |
Density |
8.94 g/cm3 |
0.323 lb/in3 |
Melting point |
2140°F |
1171°C |
Chemical Composition of Copper Nickel 90/10 Pipes & Tubes
Grade |
Cu |
Mn |
Pb |
Ni |
Fe |
Zn |
Cu-Ni 90-10 |
88.6 min |
1.0 max |
.05 max |
9-11 max |
1.8 max |
1 max |
Mechanical Properties of Cu-Ni 90/10 Pipes and Tubing
Properties |
Metric |
Imperial |
Tensile strength, ultimate |
303-414 MPa |
43900-60000 psi |
Tensile strength, yield (depending on temper) |
110-393 MPa |
16000-57000 psi |
Elongation at break (in 254 mm) |
42.00% |
42.00% |
Machinability (UNS C36000 (free-cutting brass) = 100%) |
20% |
20% |
Shear modulus |
52.0 GPa |
7540 ksi |
Poisson's ratio |
0.34 |
0.34 |
Elastic modulus |
140 GPa |
20300 ksi |
Physical Properties of Cupro Nickel 90/10 Pipes & Tubes
Properties |
Metric |
Imperial |
Density |
8.94 g/cm3 |
0.323 lb/in3 |
All copper nickel alloys consist of only one phase as the copper nickel binary system exhibits complete solid solubility
Applications of Copper Nickel alloys:
Sea Water Condensor Systems And Desalination Plants
Due to the good resistance to sea water corrosion, the copper nickel alloy Copper 90/10 and copper nickel alloy Copper 70/30 are employed for sea water condenser systems and in desalination plants, as well as pipe work in chemical plants.
Automotive Applications
Due to the fact that the copper nickel alloy Copper 90/10 requires no surface protection and hence gives extra safety, this copper nickel alloy is being increasingly employed for brake and hydraulic suspension systems and cooling systems in cars and commercial vehicles.
Marine Applications
The good resistance to biofouling and sea water corrosion resistance of the copper nickel alloys, Copper 90/10 and Copper 70/30 alloys have lead to its use in applications such as cladding for ships' hulls, legs of oil rig platforms and sea water intake screens.
Coins
The copper nickel alloys composed of copper with 25% nickel with 0.05-0.4% manganese is commonly used for the manufacture of coins, medals and other semi valuable applications.
Resistance Wire
Due to the very low temperature co-efficient of electrical resistivity, the copper nickel alloys composed of copper with 45% nickel alloy is used for resistance wire in high precision resistors. This property of copper nickel alloys allows the resistor to operate at almost exactly the same resistance regardless of temperature.
Thermocouples
The copper nickel alloys composed of copper-45% nickel alloy is also used for thermocouples as it develops a high and uniform EMF when coupled with other metals such as copper and iron.
Other
Copper nickel alloys are also used in cooling circuits, ammunition, sea water corrosion-resistant assemblies, condenser tubes. Other Applications"
Desalination units
Property Table of Copper Nickel Alloys
lammability |
5 |
Fresh Water |
5 |
Organic Solvents |
5 |
Oxidation at 500C |
3 |
Sea Water |
5 |
Strong Acid |
2 |
Strong Alkalis |
5 |
UV |
5 |
Wear |
5 |
Weak Acid |
4 |
Weak Alkalis |
5 |